Steel round bar DIN 16MnCr5 SH (1.7131) 34 mm , BG DIN DIN 17210 Alloy Rod

Steel round bar DIN 16MnCr5 SH (1.7131) 34 mm , BG DIN DIN 17210 Alloy Rod

EN 1.7131 Steel 16MnCr5 Material

EN 1.7131 steel (16MnCr5 material) is an European standard carburized steel (case hardening steel) with good hardenability and machinability. For larger cross-section parts, high surface hardness and wear resistance can be obtained after heat treatment, and low-temperature impact toughness is also high. For specification and datasheet, please see the tables below.

16MnCr5 steel is generally used after carburizing and quenching, and is mainly used for manufacturing gears, worms, sealing bushings and other components.

Datasheet

The following tables show material 16MnCr5 datasheet and specification including chemical composition, mechanical properties, etc.

(DIN EN 1.7131 Material) 16MnCr5 Steel Chemical Composition

The following table shows chemical composition of 16MnCr5 material (1.7131 steel).

Mechanical Properties of 1.7131 Steel (16MnCr5 Material)

1.7131 material, 16MnCr5 steel Brinell hardness

• Soft annealed: ≤ 207 HBW
• Treated to hardness: 156-207 HBW
• Treated to ferrite-pearlite structure and hardness: 140-187 HBW
• Normalized: 138-187 HBW

EN 1.7131, 16MnCr5 Tensile strength (after hardening and tempering at 200 °C)

• Dia. ≤ 16mm: Min. 1000 MPa
• 16 < Dia. ≤ 40mm: Min. 800 Mpa
• 40 < Dia. ≤ 100mm: Min. 600 Mpa

Heat Treatment Specification of 16MnCr5 (1.7131 Steel)

• End quench test Austenitizing temperature: 870℃ (30-35 minutes)
• Carburizing temperature: 880-980 ℃
• Core-hardening temperature: 860-900 ℃
• Case-hardening temperature: 780-820 ℃
• Tempering: 150 – 200 ℃ (≥ 1 hour)

Equivalent Grade

EN 1.7131 material (16MnCr5 steel) equivalent to ISO, US ASTM AISI SAE, Japanese JIS and Chinese GB standard. (For reference)

(a) and (b): The chemical composition has big difference compared with EN 10084.

Jiangsu Mittel Steel Industrial Limited is  located in Wuxi City,  a beautiful city near Shanghai.  Wuxi is close to  Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transportation. , Wuxi become the biggest  stainless steel sheet ,plate and coil  supply Centers in China. Jiangsu Mittel Steel Industrial Limited was established in 1998 years. as one of the largest stockists and manufacturers of industrial grade Stainless Steel products and derivatives in Wuxi ,We keep a stock of 50000 tons every month, so we can delivery goods in fast time.

Our company supplies cold/hot-rolled stainless steel sheets,stainless steel coils and stainless steel Plate to many steel factories from athome and abroad, including Shanxi Taigang Iron& Steel CO, . Ltd (TISCO)Zhangjiagang Pohang (ZPSS), Shanghai BAO STEEL, Ningbo Baoxin and steel factories in Taiwan area, Mainland Chinese and foreign countries and regions. 

Our long-term business lines are 201.202.304(1.4301).304L.316.316L(1.4404).430.409L, 309S ,310S(1.4845).317L.904L.S31803(1.4462).S32750.S32760, Finish: 2B, BA, NO. 1 NO. 4, HL, 8K and so on...Meanwhile, our company is also engaged in the long-term supply of homemade & imported medium and thick plates, galvanized and carbon steel products. 

Adhering to the principle of "quality first and customer foremost",our company will offer long-term service to nationwide manufacturers of household appliances, elevators, tableware, ornaments, tanks and machines. We can offer precise frosted wiredrawing, 8K mirror finishing and skim board oil-abrasion of various specifications at any time. The precisely-processed products will meet your requirements for high quality. Our company is a modern enterprise integrating distribution and storage. 

If you are interested in any of our products or would like to discuss a custom order, please feel free to contact us. We are looking forward to forming successful business relationships with new clients around the world in the near future.